Yazar "Bayram, Umit" için listeleme
-
Directional Solidification of Al-Si-Ti Irregular Ternary Eutectic Alloy and Thermophysical Properties
Bayram, Umit (SPRINGER, 2022)Directional solidification of Al–11.75 wt pct Si–2.15 wt pct Ti irregular eutectic alloy which has an 843.83 K melting point, was done with different growth rates (V = 8.51 to 2065.18 µm s−1) at a temperature gradient (G) ... -
Effect of Sn contents on thermodynamic, microstructure and mechanical properties in the Zn-90-Bi-10 and Bi-88-Zn-12 based ternary alloys
Esener, Pinar Ata; Altintas, Yemliha; Bayram, Umit; Ozturk, Esra; Marasli, Necmettin; Aksoz, Sezen (SPRINGER, VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS, 2019)The thermal conductivity variations with temperature for Zn90-x-Sn-x-Bi10 (x=5,10, 40 and 85wt%) and Bi88-x-Sn-x-Zn-12 (x=1.39, 43.26 and 79.3wt%) alloys were measured by using the linear heat flow method. From thermal ... -
Investigations of Electrical Resistivity and Thermal Conductivity Dependences on Growth Rate in the Al-Cu-Ti Eutectic Alloy
Marasli, Necmettin; Bayram, Umit (SPRINGER/PLENUM PUBLISHERS233 SPRING ST, NEW YORK, NY 10013, 2021)Directional solidification of Al-Cu-Ti (Al-33wt%Cu-0.1wt%Ti) eutectic alloy was done with a growth rate range (V = 8.58 to 2038.65 mu m.s(-1)) at a temperature gradient of 6.45 K.mm(-1) using Bridgman-type directional ... -
The variations of electrical resistivity and thermal conductivity with growth rate for the Zn-Al-Cu eutectic alloy
Marasli, Necmettin; Bayram, Umit; Aksoz, Sezen (SPRINGERVAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS, 2021)The Zn-Al-Cu alloy (Zn-5wt%Al-0.5wt%Cu) is solidified with different growth rates (V = 8.45-2087.15 mu m s(-1)) at a constant temperature gradient (G = 3.67 K mm(-1)) using Bridgman-type directional solidification apparatus ...